Extracting precious metals from slag using high-temperature chlorination technology

Slag high-temperature chlorination volatilization technology has unique potential in treating precious metals (such as gold, silver, platinum group metals, etc.), but it needs to be optimized according to the characteristics of precious metals. The following is a specific analysis:

1. The basic principle of chlorination volatilization of precious metals

Precious metals (Au, Ag, Pt, Pd, etc.) can be converted into volatile chlorides under high-temperature chlorination conditions, but the reaction conditions are relatively harsh:

- Gold (Au): A strong oxidizing atmosphere (such as Cl?+O?) is required to generate AuCl? (sublimation point 254°C), but it is easy to decompose at high temperature (>300°C).

- Silver (Ag): AgCl (boiling point 1564°C) is generated, but it is easy to melt at high temperature and needs to be combined with a reducing agent (such as C) to promote volatilization.

- Platinum group metals (Pt, Pd, etc.): high temperature (>800°C) and excess Cl? are required to generate PtCl? and PdCl?, but the thermal stability is low and rapid condensation is required.

Key reaction formula:

- 2Au + 3Cl2 → 2AuCl3 (oxidizing atmosphere required)

- Ag2O + 2Cl2 → 2AgCl + O2

- Pt + 2Cl? →PtCl4 (easy to decompose at high temperature)

2. Key points of precious metal recovery process

(1) Chlorination agent selection and optimization

- Cl? gas: the most efficient, but the oxidizing property needs to be precisely controlled (to avoid AuCl? decomposition).

- Mixed chlorination agent: Cl? + air (enhanced oxidizing property) or Cl? + CO (reducing property, promoting AgCl volatilization).

- Solid chlorination agent: such as NaCl + CaO (requires high temperature and carbon assistance, suitable for complex slag).

(2) Temperature and atmosphere control

- Segmented temperature control:

- Low temperature section (200-400°C): Prioritize volatilization of AuCl? (needs rapid condensation to avoid decomposition).

- Medium and high temperature section (600-900°C): Recover AgCl, PtCl?, etc.

- Atmosphere control:

- Oxidizing atmosphere (Au recovery): Pass O? or air.

- Reducing atmosphere (Ag recovery): Pass CO or H? to prevent AgCl from melting.

(3) Slag pretreatment

- Precious metal occurrence state: If encapsulated in silicate, acid leaching or roasting pretreatment is required to release the metal.

- Particle size refinement: Crushed to <100 μm to increase the reaction contact area.

3. Key challenges and solutions

(1) Low efficiency of precious metal volatilization

- Problem: AuCl? is easy to decompose at high temperature, and AgCl is easy to melt.

- Countermeasures:

- Rapid condensation (quenching device or low temperature trap).

- Adding catalyst (such as CuCl? to promote Au chlorination).

(2) Difficulty in separation of multiple metals

- Step condensation: Utilize the difference in boiling points of different chlorides (such as AuCl? volatilizes before AgCl).

- Selective chlorination: Control the Cl? concentration and temperature to preferentially chlorinate precious metals.

(3) Environmental protection and corrosion issues

- Tail gas treatment: NaOH solution absorbs Cl? and HCl, and activated carbon adsorbs residual precious metal vapor.

- Equipment corrosion protection: Use Hastelloy, graphite lining or ceramic coating reactor.

4. Application scenarios and cases

- Electronic waste: Waste circuit boards contain Au and Ag, which can be extracted by high temperature chlorination (Cl?+air, 800°C).